| Alloy Name | |
| AMW | CuZn10 |
| 22 IS | CuZn10 |
| DIN CEN/TS | CW501L |
| 13388 UNS | C22000 |
| JIS | C2200 |
| This alloy is as per the RoHS Specification | |
CuZn10 has very good cold forming properties and is well suited for e.g. coinage, beating, embossing. This alloy has a higher strength as pure copper. It has good welding and brazing properties as well as a good corrosion resistant and is not fragile to stress corrosion and dezincification. CuZn10 is principally used in jewellery, metal goods, watch industry and in electronic industry for installation parts.
| Chemical Composition | Weight percentage |
| Cu | 89.0 - 91.0 % |
| Pb | 0.05 % |
| Fe | 0.05 % |
| Zn | Remainder % |
| Total Impurity | 0.13 % |
| Main Applications |
| Electrical : Wave guides,Rotor Bar-AC Motors,Cable Warp |
| Consumer : House for Lipstick compacts, Costume Jewelry,Ball point Pens. |
| Fasteners : Screw Shells ,Bolts,Line Clamps,Rivets |
| Typical Applications : Jewellery and metal good, Components for the electrical industry,Leadframes. |
| Physical Properties Typical values in annealed temper at 20 °C | ||
| Density | 8.80 | g/cm3 |
| Thermal expansion coefficient -191 .. 16 | 9.0 | 10-6/K |
| Specific heat capacity - 0 .. 300°C | 18.2 | 10-6/K |
| Thermal conductivity | 0.376 | J/(g•K) |
| Electrical conductivity (1 MS/m = 1 m/(O mm²) | 184 | W/(m•K) |
| Electrical conductivity (IACS) | 43 | MS/m % |
| Thermal coefficient of electrical resistance (0 .. 200 C) | 1.8 | 10-3/K |
| Modulus of elasticity ( 1 GPa = 1 kN/mm²) cold formed | 99....115 | GPA |
| Mechanical Properties (EN 1652) | ||||
| Temper | Tensile Strength Rm MPa(N/mm2) |
Yield Strength Rp0.2 MPa(N/mm2) |
Elongation A50mm % |
Hardness HV |
| O (SOFT) | 245 Min | 140 | 35 Min | 75 Max |
| HB (half Hard) | 310 Min | 200 | 7 Min | 95 Min |
| HD (Hard) | 350 Min | 290 | 3 Min | 110 min |